Virgin PA66 GF 30% Resin Polyamide for Vehicle

• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Gravity: 1.16
• Izod Impact Strength: 32 J/M
• Model NO.: PA66
• Dielectric Strength: 27.2 Kv/mm
• Impact Strength: 85MPa
• Heat Deflection Temperature: 70ºC
• Flexural Modulus: 3450MPa
• Tensile Rate (Rupture Point): 10%
• Transport Package: 25kg/Bag with PP/PE Krafter Complex Bag
• Trademark: leveling
• Origin: China
• HS Code: 3908101190
• Production Capacity: 500000ton

Product Description

Virgin and Regrind Nylon 66 Resin/PA66 Granules/Polyamide 66 Pellets/PA66 Chips transparent color 
 
 

Product name

PA6/PA66 reinforced with (5%-55%)GF / (10%-50%)toughness /(V0,V1,V2)FR/ UV

 
PA66 Resin Application:
Communication, electronics, electrical appliance, household appliance and sports products etc.
 
PA66 Resin Specification:
 

Item				MB212LST XXX
		Test Method	Units	Test Result
Physical properties	Specific Gravity	ASTM D792	-	1.08
	Molding Shrinkage	ASTM D955	%	2.5
	Tensile Strength	ASTM D638	kg/cm²	400
	Flexural Strength	ASTM D790	kg/cm²	550
	Flexural Modulus	ASTM D790	kg/cm²	16000
	Izod Impact Strength	ASTM D256	kg/cm²	80
	Heat Distortion temperature	ASTM D648	(18.6kg/cm²)ºC (4.6kg/cm²)ºC	50

TEST ITEM: PA66 GF40	STANDARD	UNIT	CONDITION	TYPICAL VALUE
Density	ISO1183	g/cm3		1.47
Tensile Strength	ISO527	MPa	50mm/min	225
Tensile Elongation @ Break	ISO527	%	50mm/min	3
Flexual Strength	ISO178	MPa	2mm/min	310
Flexural Modulus	ISO178	MPa	2mm/min	10000
Charpy Impact Strength, Notched	ISO179 /1	KJ/m2	4mm, 23 °C	12
Heat Deflection Temperature	ISO75	°C	1.82MPa, 4mm	250
Flammability	UL94			HB

 
PROCESSING TIPS

 
-Drying: 4-6 hrs @ 70-90 °C
-Melt Temperature:
Feed Zone 265-275 °C Compression Zone 275-290 °C Front Zone 285-295°C
-Mold Temperature: 70-90 °CPRODUCT PROPERTIES
AG40E is 40% glass fiber reinforced nylon 66, PA66 resin, specially formulated to the application requiring high stiffness. It delivers verall balance of strength, stiffness and toughness combined with excellent chemical and abrasion resistance.  
 
TYPICAL APPLICATION
Automotive, mechanical parts, gears, plastic bush, etc
 
OUR COMPOUNDS WITH PA66:

Injection molding PA66; Filled PA66; 10-50% Glass reinforced PA66; Flame retardant PA66; Alloy blends.