Molecular Principal Chain: | Element Organic Polymer |
---|---|
Color: | White |
Synthetic Resin: | Polyurethane Resin |
Natural Resin: | Rosin |
Characteristic: | Thermosetting Resin |
Material: | Raw Plastic Material |
Customization: |
---|
Suppliers with verified business licenses
Specifications
pp hdpe ldpe granules with SGS certificate
PP HDPE LDPE LLDPE
plastic granule
SGS
FREE SAMPLE
pp hdpe ldpe granules with SGS certificate
PP HDPE LDPE LLDPE
plastic granule
SGS
FREE SAMPLE
Specification:
Properties |
Unit |
Test method |
Value |
Melt Flow Rate |
|
|
|
Melt flow rate(230°C/2.16KG) |
g/10min |
ISO 1133 |
12 |
Mechnical Properties |
|
|
|
Tensile modulus of elasticity(v=1mm/min) |
Mpa |
ISO 527-2 |
1550 |
Tensile yield at stress(v=50mm/min) |
Mpa |
ISO 527-2 |
35 |
Tensile yield at strain (v=50mm/min) |
% |
ISO 527-2 |
8 |
Tensile strain at break (v=50mm/min) |
% |
ISO 527-2 |
>50 |
Charpy impact strength unnotched(+23°C) |
kJ/m2 |
ISO 179/1eU |
110 |
Charpy impact strength notched(+23°C) |
kJ/m2 |
ISO 179/1eA |
3.0 |
Izod Impact strength notenched(+23°C) |
kJ/m2 |
ISO 180/1A |
3 |
Ball indentation hardness(H 358/30) |
Mpa |
ISO 2039-1 |
78 |
|
|
|
|
PP Copolymer
Tests |
Value |
Unit |
Melt Flow Rate |
45 |
g/10min |
Density |
0.90 |
G/cm3 |
Elongation Stress |
10 |
% |
Flexural modulus |
14 |
Mpa |
Rockwell hardness |
95 |
R scale |
IZOD impact strength |
6.5 |
kg.cm/cm |
Vicat softening point |
152 |
°C |
Heat distortion temperature |
125 |
°C |
5. Application:
1)Injection: valve, fittings, crates, automotive, closure, appliances, kettles, food containers, housewares, toys, non-prefilled syringe.
2)Extrusion: thick sheet, sheet, pipe, straw, strapping, Stationery sheet, BOPP Film, thin sheet, band.
3)Blow Molding: bottles.
4)Thermoforming: tray, bowl, jelly cup, water cups.
5)Flat yarn: woven bag, jumbo bag, carpet.
6)Fiber: multifilament, carpet, Spundbond, non-wovens.